| 304 |
304 Quality 304 is the basic type of stainless steel. This steel type withstand up to 600-6500C of oxidation. They have a very good mechanical and frictional resistance. r |
They are preferred in Chemistry, Petro-chemistry, Food, Kitchen, Automotive Industries, Medical Industry, Boiler and Heat Exchanger Production. Shiny, PVC-coated, stony and patterned types are used in all types of decoration. |
| 304 L |
304 L It is the low carbon version of TP 304. ıt has no frictional resistance against the temperatures higher than 500 0C. It has a high oxidation resistance up to 450 0C. |
It is preferred in Chemistry, Mining, Oil Industry and chemical storage tanks. This type is generally used at the temperatures lower than 400 0C. |
| 309 |
This stainless steel type can withstand fire up to 850 0C. It is preferred in furnace parts, Fuel and Private Pipelines as well as Oil Refining. |
It is preferred in furnace parts, Fuel and Private Pipelines as well as Oil Refining. |
| 310 |
This type has a high oxidation resistance at temperatures up to 1100 0C. |
It is preferred in furnace parts, Fuel and Private Pipelines, Paint Industry as well as Oil Refining. |
| 316 |
It is preferred in furnace parts, Fuel and Private Pipelines, Paint Industry as well as Oil Refining. |
This type is preferred in Chemistry, Petro-chemistry, Food, Textile, and Paper Industry. It is also preferred under marine and industrial conditions. |
| 316 L |
It is the low carbon version of TP 316. ıt has no frictional resistance at temperatures higher than 500 0C, but has a high oxidation resistance at temperature up to 450 0C. |
This type is preferred in Chemistry, Petro-chemistry, Food, Textile, and Paper Industry. It is also preferred under marine and industrial conditions and generally used at temperatures lower than 400 0C. |
| 316 TI |
It’s general corrosion resistance is rather similar to TP 316. It has a high oxidation resistance at temperatures up to 650 0C. |
This type is generally preferred in Chemistry, Petro-chemistry, Textile, and Paper Industry. |
| 310 S |
It is fairly similar to TP 304. It has a little better mechanical and corrosion resistance. This type enables precise welding works and provides a highly temperature oxidation resistance at temperatures up to 1200 0C. |
It is preferred in furnace parts, Fuel and Private Pipelines, Paint Industry as well as Oil Refining. |
| 321 |
It ensures inter-crystal corrosion resistance thanks to the TI addition it contains. This type has a high oxidation resistance at temperatures up to 900 0C. This material has a perfect mechanical and frictional resistance. |
It is generally used in Resistance and Exhaust Pipes, Manifold, Plane Parts, Industrial Boiler Parts, Printing Blades and Salt Machine. |
| 420 |
This type does not contain nickel and it can be magnetized. |
It is used for producing knives/blades. |
| 430 |
It provides a good surface appearance and can be magnetized as it does not contain nickel. |
Thy type is generally preferred in Tableware, interior decoration applications etc. |
| 430 TI |
It provides optimum corrosion resistance thanks to the TI addition it contains. It has a better thermal conductivity in proportion to TP304. |
This type is preferred in hot water systems, hot water tanks and sugar industry. |
| 409 |
It can withstand high temperatures and corrosion. |
This type is generally preferred for producing exhaust pipes. |