Martenzit Paslanmaz Çeliklerin Kimyasal Kompozisyonu.
AISI Kompozisyon (%)
C Cr Diğerleri
403 0,15 11,5 - 13,0 0,5 Si
410 0,15 11,5 - 13,5
414 0,15 11,5 - 13,5 1,25 - 2,5 Ni
416 0,15 12,0 - 14,0 1,25 Mn, 0,15 S (min.), 0,060 P, 0,60 Mo (opt.)
416 Se 0,15 12,0 - 14,0 1,25 Mn, 0,060 P, 0,15 Se (min.)
420 0,15 (min.) 12,0 - 14,0
431 0,2 15,0 - 17,0 1,25 - 2,5 Ni
440 A 0,60 - 0,75 16,0 - 18,0 0,75 Mo
440 B 0,75 - 0,95 16,0 - 18,0 0,75 Mo
440 C 0,95 - 1,20 16,0 - 18,0 0,75 Mo

Ferritik Paslanmaz Çeliklerin Kimyasal Kompozisyonu.
Kompozisyon (%)
C Cr M Diğerleri
406 0,08 11,5 - 14,5 1,0 0,1 - 0,3 Al
430 0,12 14,0 - 18,0 1,0 0,060 P, 0,15 S (min.), 0,60 Mo (opt.)
430F 0,12 14,0 - 18,0 1,25 0,060 P, 0,060 S, 0,15 Se (min.)
430FSe 0,12 14,0 - 18,0 1,25
442 0,2 18,0 - 23,0 1,0
446 0,2 23,0 - 27,0 1,5 0,25 N
Tekli rakamlar max. %'leri gösterirler. Belirtilen miktarların diğer alaşımları max. değerleri içerirler; kalanı demirdir.

Ferritik Paslanmaz Çeliklerin Mekanik Özellikleri.
AISI Oda sıcaklığı Çalışma sıcaklığı Fo
Çekme kuvveti (1000 psi) Akma kuvveti 0,2% (1000 psi) Uzama 2 in. (%) Sertlik (Rockwell B') Devamlı Kesintili
406 70 40 30 81 1400 1450
430 75 45 30 83 1550 1660
430F, 430FSe 80 55 25 87 1500 1600
442 80 45 20 90 1800 1900
446 80 50 25 86 1950 2060

Ostanitik Paslanmaz Çeliklerin Kimyasal Kompazisyonu.
Kompozisyonu (%)
C Cr Ni Diğerleri (%)
201 0,15 16,0 - 18,0 3,5 - 5,5 2.5 N, 5.5 - 7.5 Mn, 0.060 P
202 0,15 17,0 - 19,0 4,0 - 6,0 2.5 N, 7.5 -10.0 Mn, 0.060 P
301 0,15 16,0 - 18,0 6,0 - 8,0
302 0,15 17,0 - 19,0 8,0 - 10,0
302 B 0,15 17,0 - 19,0 8,0 - 10,0 2.0 - 3.0 Si
303 0,15 17,0 - 19,0 8,0 - 10,0 0.20 P, 0.15 S (min) 0.60 Mo (opt)
303 Se 0,15 17,0 - 19,0 8,0 - 10,0 0.20 P, 0.06 S, 0.15 Se (min)
304 0,08 18,0 - 20,0 8,0 - 12,0
304 L 0,03 18,0 - 20,0 8,0 - 12,0
305 0,12 17,0 - 19,0 10,0 - 13,0
308 0,08 19,0 - 21,0 10,0 - 12,0
309 0,02 22,0 - 24,0 12,0 - 15,0
309 S 0,08 22,0 - 24,0 12,0 - 15,0
310 0,25 24,0 - 26,0 19,0 - 22,0 1.5 Si
310 S 0,08 24,0 - 26,0 19,0 - 22,0 1.5 Si
314 0,25 23,0 - 26,0 19,0 - 22,0 1.5 - 3.0 Si
316 0,08 16,0 - 18,0 10,0 - 14,0 2.0 - 3.0 Mo
316 L 0,03 16,0 - 18,0 10,0 - 14,0 2.0 - 3.0 Mo
317 0,08 18,0 - 20,0 11,0 - 15,0 3.0 - 4.0 Mo
321 0,08 17,0 - 19,0 9,0 - 12,0 Ti (5 x %C min)
347 0,08 17,0 - 19,0 9,0 - 13,0 Cb + Ta (10 x %C min)
348 0,08 17,0 - 19,0 9,0 - 13,0 Cb + Ta (10 x %Cmin 0.10 Ta max.), 0.20 Co
Tekil rakamlar aksi belirtilmedikçe en yüksek miktarlardır. Belirtilen alaşımların diğer elemanları en yüksek miktarları içerirler, geriye kalan yüzde demirdir.

Ostanitik Paslanmaz Çeliklerin Mekanik Özellikleri
Oda Sıcaklığı Çalışma Sıcaklığı Fo
Çekme Kuvveti (1000 Psı) Akma Kuvveti 0.2 % (1000 Psı) Uzama 2" (%) Sertlik (Rockwell B') Devamlı Kesintili
201 115 55 55 90 1550 1450
202 105 55 55 90 1550 1450
301 110 40 60 85 1650 1500
302 90 40 50 85 1650 1500
302 B 95 40 55 85 1750 1600
304 84 42 55 80 1650 1550
304 L 81 39 55 79 1650 1550
305 85 38 50 80 1650
308 85 35 50 80 1700 1550
309 90 45 45 85 1950 1850
310 95 45 45 85 2050 1900
314 100 50 40 85
316 84 42 50 79 1650 1550
316 L 81 42 50 79 1650 1550
317 90 40 45 85 1700 1600
321 90 35 45 80 1650 1550
347 95 40 45 85 1650 1550